Abstract: The aim of the study was to evaluate how the association of solvents (tetrahydrofuran [THF], dimethyl sulfoxide [DMSO], ethanol [ET] or acetone [ACT]) with experimental dental adhesives affects selected properties of experimental dental adhesives and dentin bond durability. Six adhesive combinations were prepared containing: 30 % ET, 30 % ACT, 30 % THF, 28 % ET + 2 % DMSO (ET+DMSO), 15 % ethanol + 15 % THF (ET+THF), or 28 % THF + 2 % DMSO (THF+DMSO). Thirty-six molars (n = 6) were cut to expose the coronary dentin, and were randomly divided according to the adhesives. They were restored, and then cut into resindentin sticks (1 mm²), and stored in distilled water for 24 h or 6 months, until conducting the microtensile bond strength and nanoleakage tests. Other experiments performed with adhesives included viscosity assessment using a rheometer, and degree of conversion using Fourier-transform infrared spectroscopy (FTIR). The data were analyzed statistically using two-way ANOVA and Tukey’s test (p < 0.05). The adhesive formulated exclusively with THF showed the highest viscosity, followed by ET+THF, which obtained the highest degree of conversion compared to ET, and THF alone. ET+DMSO obtained the highest 24-h and aged bond strengths (p < 0.05). ET+THF increased the nanoleakage slightly after 6 months, but attained the only gap-free adhesive interface among all the groups. The combination of alternative solvents, particularly THF, with conventional ones (ET) has improved chemical properties, and the dentin bonding of experimental simplified adhesives.

RESUMO Objetivo: Avaliar e comparar a precisão dimensional de três técnicas de moldagem: dupla mistura, reembasamento e moldeira individual. Métodos: Um modelo metálico inferior parcialmente edêntulo foi fabricado com pontos de referência nos dentes e usado para fazer as moldagens. As distâncias ântero-posteriores e transversais foram medidas. Todas as moldagens foram feitas com um silicone por adição utilizando moldeiras metálicas (técnicas da dupla mistura e reembasamento) ou de resina acrílica (técnica da moldeira individual). Na técnica da moldeira individual foi utilizado apenas o elastômero de viscosidade leve e nas técnicas da dupla mistura e reembasamento foram usados os elastômeros nas viscosidades denso e leve. Após os procedimentos de moldagem, a precisão dimensional de cada técnica de moldagem foi avaliada aferindo os modelos de gesso (n = 5) em um microscópio comparador com 30x de aumento e 0,5 µm de precisão. Os dados foram analisados estatisticamente por ANOVA dois fatores e teste de Tukey (p<0,05). Resultados: Os modelos de gesso feitos com todas as técnicas de moldagem apresentaram alterações lineares negativas (contração). As distâncias ântero-posteriores apresentaram maiores alterações dimensionais que as distâncias transversais. O lado parcialmente edêntulo teve maior contração que o lado ântero-posterior oposto. Conclusão: Não foram encontradas diferenças entre as técnicas de moldagem, mas foram observadas significantes alterações dimensionais.

ABSTRACT Objective: The purpose of this in vitro study was to assess and compare the dimensional accuracy of three impression techniques: 1-step putty/light-body, 2-step putty/light-body, and the monophase technique. Methods: A partially edentulous standard stainless steel mandibular arch cast with reference points on the teeth was used to make the impressions. The anteroposterior and transverse distances were measured. All impressions were made with a polyvinyl siloxane using stock metallic (1- and 2-step putty/light-body techniques) or acrylic resin (monophase technique) trays. The monophase impressions were made using a light-body material and the 1- and 2-step putty/light-body impressions with putty and light-body materials. After impression procedures, the accuracy of each technique was assessed measuring the stone casts (n = 5) poured from the impressions using a microscope at 30x magnification and at 0.5 µm accuracy. The data were analyzed statistically using 2-way ANOVA and Tukey's test (p<0.05). Results: Stone casts made by all techniques had significantly negative linear changes (shrinkage). The anteroposterior distances showed more dimensional changes than the transverse distances. The edentulous side showed more shrinkage than the anteroposterior side. Conclusion: No differences between the impression techniques were found, but significant dimensional changes were observed.

Resumo O objetivo neste estudo foi verificar a resistência de união em restaurações simuladas de compósitos baseados em metacrilato ou silorano reparadas com compósito à base de metacrilato. Compósitos baseados em metacrilato (Filtek P60; 3M ESPE) ou silorano (Filtek P90; 3M ESPE) foram associados com adesivo (Adper Single Bond 2; 3M ESPE). Vinte e quatro amostras em forma de semi-ampulhetas foram reparadas com cada material (n=12), conforme os grupos experimentais: G1- P60 + Adper Single Bond 2 + P60; G2- P60 + Adper Single Bond 2 + P60 + termociclagem; G3- P90 + Adper Single Bond 2 + P60; e G4- P90 + Adper Single Bond 2 + P60 + termociclagem. Os grupos G1 e G3 foram submetidos ao ensaio de tração após 24 horas do procedimento de reparo e os grupos G2 e G4 depois de submetidos a 5.000 ciclos térmicos de 5 e 55 ?#61616;C por 30 s em cada banho. O teste de resistência à tração foi efetuado em máquina universal atuando numa velocidade de 0,5 mm/min. Os dados (MPa) foram submetidos a ANOVA a dois fatores e teste de Tukey (5%). O padrão de fratura das amostras (adesivo, coesivo em resina ou misto) foi avaliado em estereomicroscópio com aumento de 30x e imagens representativas foram obtidas em MEV. Os valores de resistência à tração das amostras feitas com compósito à base de metacrilato e reparadas com compósito à base de metacrilato (G1 e G2) foram maiores do que nas amostras feitas com compósito à base de silorano e reparadas nas mesmas condições (G3 e G4). A termociclagem diminuiu os valores de resistência à tração para ambos os compósitos. Todos os grupos mostraram predominância de fraturas adesivas e nenhuma falha coesiva foi observada em compósito. Em conclusão, valores maiores de resistência à tração foram observados em amostras de resina à base de metacrilato e maior porcentagem de fraturas adesivas nas amostras de resina à base de silorano, ambos os compósitos reparados com resina à base de metacrilato.

Abstract The study verified the bond strength in simulated dental restorations of silorane- or methacrylate-based composites repaired with methacrylate-based composite. Methacrylate- (P60) or silorane-based (P90) composites were used associated with adhesive (Adper Single Bond 2). Twenty-four hemi-hourglass-shaped samples were repaired with each composite (n=12). Samples were divided according to groups: G1= P60 + Adper Single Bond 2+ P60; G2= P60 + Adper Single Bond 2 + P60 + thermocycling; G3= P90 + Adper Single Bond 2 + P60; and G4= P90 + Adper Single Bond 2 + P60 + thermocycling. G1 and G3 were submitted to tensile test 24 h after repair procedure, and G2 and G4 after submitted to 5,000 thermocycles at 5 and 55 ?#61616;C for 30 s in each bath. Tensile bond strength test was accomplished in an universal testing machine at crosshead speed of 0.5 mm/min. Data (MPa) were analyzed by two-way ANOVA and Tukey's test (5%). Sample failure pattern (adhesive, cohesive in resin or mixed) was evaluated by stereomicroscope at 30?#61655; and images were obtained in SEM. Bond strength values of methacrylate-based composite samples repaired with methacrylate-based composite (G1 and G2) were greater than for silorane-based samples (G3 and G4). Thermocycling decreased the bond strength values for both composites. All groups showed predominance of adhesive failures and no cohesive failure in composite resin was observed. In conclusion, higher bond strength values were observed in methacrylate-based resin samples and greater percentage of adhesive failures in silorane-based resin samples, both composites repaired with methacrylate-based resin.

O objetivo deste estudo foi avaliar a eficácia de diferentes condicionamentos de superfície na resistência de união de reparos de compósitos restauradores em três tipos de cerâmicas odontológicas: reforçada por dissilicato de lítio, reforçada por leucita e feldspática. Foram confeccionados 12 blocos para cada tipo de cerâmica (n=3) e armazenados por 3 meses em água destilada a 37 oC. A superfície de união das cerâmicas foi regularizada com lixa de granulação 600 por 15 s e lavadas em ultrassom por 10 min. Os tratamentos de superfície para cada cerâmica foram: GC (controle) - nenhum; GPD - ponta diamantada com 30 µm de granulação; GAF - ácido hidrofluorídrico a 10%; GJ - jateamento com partículas de óxido de alumínio revestido por sílica (45 µm - tamanho das partículas). Após, foi realizada a limpeza da superfície com ácido fosfórico a 7% por 20 s, seguido de silano e adesivo. Como material restaurador foi utilizada resina composta. Após o reparo, as amostras foram submetidas a ciclagem térmica (10,000 ciclos entre 5 °C e 55 °C, por 30 s). Na sequência, as amostras foram seccionadas em palitos de aproximadamente 1,0 mm2 e levadas ao teste de tração em uma máquina de ensaios universal à velocidade de 0,5 mm/min. Os dados obtidos foram comparados estatisticamente por ANOVA de dois fatores e teste de Tukey (α=0,05). Sugere-se que o desgaste da superfície com ponta diamantada é mais indicado para a cerâmica feldspática e cerâmica reforçada por leucita, enquanto o condicionamento com ácido fluorídrico é indicado para reparos em cerâmica reforçada por dissilicato de lítio. O jateamento com partículas de óxido de alumínio revestido por sílica mostrou-se aplicável à cerâmica reforçada por leucita. Predominancia de fraturas adesivas acima de 85% foi observada para todos os grupos. Este estudo demonstrou que o sucesso dos tratamentos de superfície depende do tipo de cerâmica a que são aplicados.

The aim of this study was to evaluate the efficacy of different surface conditioning methods on the microtensile bond strength of a restorative composite repair in three types of dental ceramics: lithium disilicate-reinforced, leucite-reinforced and feldspathic. Twelve blocks were sintered for each type of ceramic (n=3) and stored for 3 months in distilled water at 37 °C. The bonding surface of ceramics was abraded with 600-grit SiC paper. Surface treatments for each ceramic were: GC (control) - none; GDB - diamond bur #30 µm; GHF - hydrofluoric acid (10%); GT- tribochemical silica coating (45-μm size particles). Treatments were followed by cleaning with phosphoric acid 37% for 20 s + silane + adhesive. The composite resin was used as restorative material. After repair, samples were subjected to thermocycled ageing (10,000 cycles between 5 °C and 55 °C for 30 s). Thereafter, the samples were sectioned into 1.0 mm2 sticks and tested for microtensile bond strength with 0.5 mm/min crosshead speed. Data were compared by two-way ANOVA and Tukey's test (α=0.05). The superficial wear with diamond bur proved to be suitable for feldspathic porcelain and for leucite-reinforced glass ceramic while hydrofluoric acid-etching is indicated for repairs in lithium disilicate-reinforced ceramic; tribochemical silica coating is applicable to leucite-reinforced ceramic. Predominance of adhesive failures was observed (>85% in all groups). In conclusion, the success of surface treatments depends on the type of ceramic to be repaired.

Esse estudo teve como objetivo avaliar a influência da incorporação de epigalocatequina-3-galato (EGCG) nas propriedades físico-químicas de um sistema adesivo à base de metacrilato. O EGCG foi adicionado ao Adper Easy One (3M-ESPE), exceto para o grupo controle, para a obtenção das concentrações de 0,01% e 0,1% p/p. No ensaio de sorção (S) e solubilidade (SL), foram confeccionados discos de resina de acordo com as recomendações da ISO (n=10). O grau de conversão (GC) foi analisado através de FTIR, enquanto a resistência flexural (RF) foi avaliada em teste de flexão de três pontos com espécimes em forma de barra (n=10). Os dados foram submetidos à Análise de Variância a um critério e teste de Tukey (p<0,05). Não houve diferença significativa entre as concentrações de EGCG testadas no GC, SL e RF (p>0,05). Adesivos contendo EGCG a 0,1% ou 0,01% apresentaram valores similares de SL (p>0,05) e maiores do que os valores obtidos pelo adesivo não incorporado por EGCG. Conclui-se que a adição de EGCG ao adesivo reduziu a solubilidade sem afetar as outras propriedades avaliadas.

This study aimed to evaluate the influence of epigallocatechin-3-gallate (EGCG) incorporation on the physicochemical properties of a methacrylate-based dental adhesive. EGCG was added to Adper Easy One (3M-ESPE) except in control group, to obtain concentrations of 0.01% w/w and 0.1% w/w of EGCG-doped adhesives. For water sorption (WS) and solubility (SL) surveys, resin discs were assayed following ISO recommendations (n=10). The degree of conversion (DC) was analyzed by FTIR whereas flexural strength (FS) was tested by three-point bending with bar specimens (n=10). Data were subjected to one-way ANOVA and Tukey's test (p<0.05). No significant difference in the DC, WS and FS were found between the different concentrations of EGCG (p>0.05). Adhesives containing 0.1% or 0.01% of EGCC demonstrated similar values of SL (p>0.05) and higher than those found for adhesive without EGCC (p<0.05). In conclusion, the addition of EGCC to adhesive reduced the solubility without affecting the other evaluated properties.